擠壓速度對(duì)6063鋁合金管材焊合強(qiáng)度的影響

擠壓速度對(duì)6063鋁合金管材焊合強(qiáng)度的影響Effect of extrusion speed on weld strength of 6063 square tube

通過建立6063鋁合金多孔分流模擠壓過程的三維有限元模型，研究不同擠壓速度下擠壓力、焊合面溫度、焊合壓力和材料有效應(yīng)力等參數(shù)的演變規(guī)律及其對(duì)焊合質(zhì)量的影響，建立預(yù)測(cè)鋁合金方管焊合質(zhì)量的評(píng)價(jià)模型，并采用膨脹實(shí)驗(yàn)驗(yàn)證模型的準(zhǔn)確性。結(jié)果表明：隨著金屬流入分流孔、焊合室和定徑帶，擠壓力逐漸增大并達(dá)到峰值，而后緩慢降低；隨著擠壓速度的增大，焊合面溫度、焊合壓力和有效應(yīng)力逐漸升高，焊合質(zhì)量系數(shù)k值逐漸降低。膨脹結(jié)果表明，最大載荷處的位移與k值呈正相關(guān)，說明所建立的k值模型具有較高的精度。

The evolution of extrusion pressure, temperature, welding pressure and effective stress of 6063 aluminum alloy were investigated under different extrusion pressures through building up three-dimensional FE simulation during porthole extrusion, and their effect on the quality of the weld seams were evaluated. The evaluation welding quality model was established and its accuracy was verified by expanding tests. FE simulation results reveal that the extrusion pressure increases with the metal flowing into the inlet ports, welding chamber and die bearing. Over the pressure peak, the extrusion pressure decreases continuously. As ram speed increasing, the temperatures, the mean stresses and the effective stresses on the welding plane in the welding chamber increase. k value shows downward trend with the ram speed increasing. Expanding tests confirm that the extrusion at higher ram speed leads to a bad bonding at the longitudinal weld seams, which corresponds to the k value.

全文下載：https://pan.baidu.com/s/1c1AAmXE