真空燒結(jié)泡沫304不銹鋼吸聲性能

真空燒結(jié)泡沫304不銹鋼吸聲性能Sound absorption property of vacuum sintered 304 stainless steel foam

利用掛漿工藝，在1050 ℃下真空燒結(jié)3 h，成功制備三維網(wǎng)狀的泡沫304不銹鋼，制品燒結(jié)良好。樣品平均孔徑約1.8 mm，孔隙率約93.7%。測試該泡沫金屬在200~6300 Hz及其加入背腔后在2500~4000 Hz時(shí)的吸聲系數(shù), 探討背腔對樣品吸聲性能的影響。結(jié)果表明：本制品在測試范圍的中高頻段表現(xiàn)出較好的吸聲效果，其第一共振頻率為4000 Hz，此時(shí)最大吸聲系數(shù)約0.7；在1250~3150 Hz之間，增加樣品厚度可明顯提高吸聲效果；加入背腔可大幅度提高樣品的整體吸聲效果。

304 stainless steel foam with the pore size of about 1.8 mm and the porosity of about 93.7% was prepared by the slurry sintering method at 1050 ℃ for 3 h in vacuum. The sound absorption coefficient was tested for the foam at 200-6300 Hz and for the back cavity composite at 2500-4000 Hz. The results show that the foam sample shows a good sound absorption in the middle and high frequency range, exhibiting the first resonance frequency of around 4000 Hz and the maximum absorption coefficient of about 0.7. The absorption performance may be obviously improved by increasing the sample thickness at 1250-3150 Hz and by adding a back cavity at 2500-4000 Hz.

全文下載：https://pan.baidu.com/s/1nwmBUaP

作為值得信賴的合作伙伴和高品質(zhì)金屬合金的半成品供應(yīng)商，通項(xiàng)公司擁有完善的服務(wù)體系和專業(yè)的團(tuán)隊(duì)。在同客戶交易的過程中，我們力求根據(jù)不同的應(yīng)用需求將我們的產(chǎn)品做到精益求精。針對當(dāng)前和未來的市場需求，通項(xiàng)公司致力于為客戶提供最佳的金屬材料解決方案。

TXCO has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. TXCO develops the best alloy material solutions for current and future challenges.

獲取更多我們供應(yīng)的產(chǎn)品和服務(wù)信息，請致電086-021-6786 0205或發(fā)電子郵件service@sinoav.com聯(lián)系我們，您也可以通過微信，微博，領(lǐng)英，臉書，推特和谷歌+與我們互動(dòng)。

For more information on the products and services that we supply, call us at 086-021-6786 0205 or email us at service@sinoav.com. You can also get in touch on social media, we are constantly active on Weixin, Weibo, LinkedIn, Facebook, Twitter and Google+.