電子束熔絲沉積快速成形2319鋁合金的微觀組織與力學(xué)性能研究

電子束熔絲沉積快速成形2319鋁合金的微觀組織與力學(xué)性能研究Microstructure and Mechanical Properties of Additive Manufactured 2319 Alloy by Electron Beam Freeform Fabrication

選用直徑2 mm的2319鋁合金絲材進(jìn)行電子束熔絲沉積快速成形，制備出150mm×35mm×52 mm的打印樣品。研究了樣品在不同方向上的微觀組織與力學(xué)性能。結(jié)果表明，通過(guò)控制電子束增材制造的參數(shù)，可獲得致密無(wú)宏觀缺陷的塊體材料，其致密度可達(dá)到99.3%。打印態(tài)2319鋁合金，平均晶粒尺寸小于10 μm，并含有初晶Al2Cu相、細(xì)小析出相和粗大雜質(zhì)相。樣品中存在少量的微小孔洞，其尺寸為5?15 μm。樣品在長(zhǎng)、寬、高3個(gè)方向的拉伸強(qiáng)度分別約為161、174和167 MPa。經(jīng)T6處理后，粗大相基本熔解，析出尺寸更細(xì)小、分布更均勻的沉淀強(qiáng)化相，孔洞尺寸有所增大。由于沉淀強(qiáng)化起了主導(dǎo)作用，T6處理后樣品力學(xué)性能顯著提高，3個(gè)方向的拉伸強(qiáng)度分別提高到約423、495和421 MPa。

2319 aluminum alloy wires with diameter of 2 mm were used for additive manufacturing (AM) by Electron beam freeform fabrication (EBF3), with a sample of 150 × 35 × 52 mm being printed. The microstructure and mechanical properties of the printed sample in three directions were investigated. The results showed that bulk materials of the 2319 alloy can be printed without macroscopic defects under selective EBF3 parameters, with a relative density of 99.3% compared to the initial wires. The average grain size is the printed sample was less than 10μm, containing primary Al2Cu phases, fine particles, and coarse impurity phases. There are some tiny voids in the printed sample, and the sizes of the voids are 5?15 μm. The ultimate tensile strength of the printed sample are 161, 174 and 167 MPa in the length, width and height directions. After a T6 treatment, the coarse phase were basically dissolved and some finer phases were re-precipitated. Due to the dominant effect of dispersion strengthening, the mechanical properties of the sample were significantly improved, and the ultimate tensile strength of the sample in three directions was increased to 423, 495, and 421MPa, respectively.

全文下載：https://pan.baidu.com/s/1VEsnayFLdss09lQ7OwEblg?

作為值得信賴的合作伙伴和高品質(zhì)金屬合金的半成品供應(yīng)商，通項(xiàng)公司擁有完善的服務(wù)體系和專業(yè)的團(tuán)隊(duì)。在同客戶交易的過(guò)程中，我們力求根據(jù)不同的應(yīng)用需求將我們的產(chǎn)品做到精益求精。針對(duì)當(dāng)前和未來(lái)的市場(chǎng)需求，通項(xiàng)公司致力于為客戶提供優(yōu)質(zhì)的金屬材料解決方案。

TXCO has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. TXCO develops the superior alloy material solutions for current and future challenges.

獲取更多我們供應(yīng)的產(chǎn)品和服務(wù)信息，請(qǐng)致電086-021-6786 0205或發(fā)電子郵件service@sinoav.com聯(lián)系我們，您也可以通過(guò)微信，微博，領(lǐng)英，臉書，推特和谷歌+與我們互動(dòng)。

For more information on the products and services that we supply, call us at 086-021-6786 0205 or email us at service@sinoav.com. You can also get in touch on social media, we are constantly active on Weixin, Weibo, LinkedIn, Facebook, Twitter and Google+.